Physical Properties |
Density (23 oC) | 951 | kg/cm3 | ISO 1183 |
MFI (190 oC /21.6Kg) | 10 | dg/min | ISO 1133 |
Mechanical properties (2) | | | |
Tensile Modulus of elasticity | 1050 | MPa | ISO527-1;2 |
Tensile Strength (MD) | 55 | MPa | ISO 527-1;3 |
Tensile Strength (TD) | 55 | MPa | ISO 527-1;3 |
Tensile Strain at Break (MD) | 580 | % | ISO 527-1 |
Tensile Strain at Break (TD) | 620 | % | ISO 527-1 |
Tensile stress at Yield | 26 | MPa | ISO 527-1 |
Tensile strain at Yield | 10 | % | ISO 527-1 |
Elemendorf tear strength(MD) | 250 | mN | ISO 6383-2 |
Elemendorf tear strength(TD) | 800 | mN | ISO 6383-2 |
Thermal Properties |
Melting Point | 132 | oC | ISO 3146 |
Vicat Temperature , (A50,50 oC/h , 10N) | 127 | oC | ISO 306 |
PRODUCT DESCRIPTION:
HFI5110 is a high molecular weight, high density polyethylene, which has a broad molecular weight distribution and high melt strength. This product specially designed for producing thin films with excellent strength and rigidity.
APPLICATIONS:
HFI5110 is recommended for blown film extrusion. This product is suitable for manufacture of high strength grocery sacks, shopping bags and high quality thin films for uni/multi-wall packaging. Films produced with this product can be readily treated and printed to give high quality graphics.
PRODUCT PROPERTIES:
Extruder temperature profile: 200-235°C Frost line height: 6-8 times die diameter. Blow Up Ratio: 3-5
Recommended film thickness: 15 to 50 μm
Please note that, these processing conditions are recommended by producer only for 100% HFI5110 resin (not in the case of blending with any other compatible material), but because of the many particular factors which are outside our knowledge and control, and may affect the use of product, no warranty is given.